Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

Control of the particle microstructure during the synthesis of bulk-polymerized transparent methacrylate-acrylonitrile-butadiene-styrene resin

A series of methacrylate-acrylonitrile-butadiene-styrene (MABS) resins was prepared using bulk polymerization. The polarity of the continuous phase and the compatibility of two phases were changed by adjusting the methyl methacrylate (MMA) content, choosing values that were close to styrene-butadiene rubber solubility value. The possibility of controlling the microstructure of the MABS resin by changing the polarity of the components and the compatibility of two phases was assessed. The dynamic mechanical analysis shows that the compatibility of two phases varies with the MMA content. The morphological analysis shows that increasing MMA contents results in a gradual decrease in the sub-inclusion structure with a network skeleton of rubber particles, and that all the particles become solid rubber when the MMA content reaches 75%. The sub-inclusion structure reappears but does not have a network skeleton when the MMA content is 90%. The impact strength and morphological analysis indicate that the solid rubber particles and the sub-inclusion structure with a network skeleton provide excellent toughness, while the sub-inclusion structure without a network skeleton does not. In contrast, the transmittance of the ABS resin first increased and then decreased with increasing MMA content.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

透明聚丙烯片材专用料研究

研究透明成核剂对均聚PP透明性能的影响。试验表明加入透明成核剂后,提高了PP的透光率,降低了雾度,力学性能得到了明显的改善,添加0.2%透明剂在160~230℃加工条件下生产的专用料,可以制得透明PP片材。     

一种高性能的新结构IGBT

提出了一种低功率损耗的新结构IGBT.该新结构的创新点在于其复合耐压层结构,该耐压层包括深扩散形成的n型缓冲层和硼注入形成的透明背发射区两部分.虽然在正常工作条件下,该新结构IGBT工作于穿通状态,但器件仍具有非穿通IGBT(NPT-IGBT)的优良特性.该新结构IGBT具有比NPT-IGBT更薄的芯片厚度,从而可以获得更好的通态压降和关断功耗之间的折衷.实验结果表明:与NPT-IGBT相比较,新结构IGBT的功率损耗降低了40%.     

用于液晶光阀空间光调制器的ITO透明导电膜的研制

本文介绍了ITO(Indium Tin Oxide)透明导电膜的制备工艺,对影响其光学和电学特性的因素作了分析。并讨论了透明导电的机理,在K9玻璃上制备的ITO透明导电膜,在500～600nm波长范围内,典型的峰值透过率为90％,面电阻为40～50Ω/□。用该技术制备的样品作为透明电极,在液晶光阀空间光调制器中得到了应用。     

Increasing Reliability in Cable-Free Radio LANs Low Level Forwarding in HIPERLAN

Radio LANs are emerging in the computing world. They are supported by distinct configurations: on the one hand radio LANs with base stations and a wired backbone, on the other hand radio LANs implementing Intra-forwarding. Adding a new node in a radio LAN with Intra-forwarding, increases the reliability, while this reliability decreases with ad hoc or hub configurations. This advantage of Intra-forwarding is quantified. Intra-forwarding, as defined in the HIPERLAN standard, is based on a hop-by-hop policy and link check procedures. It is shown how point-to-point packets and broadcast packets are forwarded. The three basic components of Intra-forwarding needed to build and update the Intra-forwarding database are described. The originality of this approach is the use of multipoint relays which enable better scalability. The correctness of the Intra-forwarding protocol is proved and its cost is evaluated.     

掺铝氧化锌(AZO)导电薄膜的研究进展

综述透明导电薄膜的性能、种类、制备工艺、研究及应用状况,重点讨论掺铝氧化锌(AZO)薄膜的结构、导电机理、光电性能和当前的研究焦点。并指出,为了进一步提高透明导电薄膜的性能,应从以材料选择、制备工艺、多层膜光学设计等方面深入研发,以满足尖端技术的需要。     

液相对流对固液界面稳定性的影响

以模型合金丁二腈－乙醇的强制性晶体生长为基础，利用自行研制的液相对流驱动装置，详细考查了液相自然对流及强迫对流作用下，模型合金平界面失稳的动态生长过程，证实了液相的流动加快了液相温度与浓度分布的均匀化，从而增强了液／固界面的稳定性。并且随流动速度的增加，界面稳定性提高。